Characteristics:  A medium alloy chromium carbide overlay for applications involving high impact combined with abrasion. Weld metal is tougher than conventional chromium carbide alloys with fewer stress relieving check-cracks.

Typical Applications:  Most applications involve high impact and crushing, such as the final overlay on crusher jaws, cone and roll shells, hammer mill hammers, impact breaker bars and pulverizing hammers.

Specifications:  
Wire Type:
Metal-cored, open-arc or gas shielded. Deposits are slag-free

Alloy Content:
Carbon, Chromium, Molybdenum, Manganese, Silicon

Hardness :  47 - 52 Rc 

Deposit Thickness: 3 - 5 layers 

Cannot be flame cut.

Standard Sizes:  
.045"(1.2mm)
1/16"(1.6mm)
7/64"(2.8mm)

Alternative Electrode:
Postalloy 213

 Characteristics:  A high carbon, high chromium hardfacing alloy that produces wear resistant chromium carbides in a tough alloy matrix that is designed for high abrasion or and abrasion combined with moderate impact.

Typical Applications: Tampers, fan blades, coal feeder screws, coal pulverizing hammers, grizzly bars, screw conveyors, bulldozer blades, dragline buckets, power shovel buckets and teeth, ore and coal chutes, road rippers, scraper blades, dredge bucket lips, dredge pump side plates, dredge cutter head & teeth, cement chutes, clamshell bucket lips, crusher jaws, crusher cones, gyratory crusher mantles and muller tires. 

Specifications:
Wire Type:
Metal-cored, open-arc or gas-shielded. Deposits are slag-free

Alloy content :
Carbon, Chromium, Manganese, Silicon, Molybdenum

Hardness:  55 - 60 Rc

Deposit Thickness : 2 to 3 layers

Deposits cannot be flame cut
Deposits will check-crack to relieve stresses 

Standard Sizes 
.045"(1.2mm)
1/16"(1.6mm)
7/64"(2.8mm)

Alternative Welding Electrode:
Postalloy 214 or 215HD